木薯淀粉接枝丙烯酸-丙烯酰胺吸水剂合成研究初探  

Preliminary study on synthesis of graft copolymerization of acrylic acid and acrylamide onto maniocca

作　　者：成青[1] 黄含玉[1] 

机构地区：[1]中南林业科技大学材料科学与工程学院,湖南长沙410004

出　　处：《现代化工》2008年第S2期265-267,共3页Modern Chemical Industry

基　　金：中南林业科技大学青年基金项目(05004A)

摘　　要：用过硫酸钾做引发剂,通过水溶液聚合法制得了木薯淀粉接枝丙烯酸和丙烯酰胺高吸水性树脂。研究了丙烯酸与丙烯酰胺用量比、反应温度及引发剂用量等对吸液性能的影响,分析了木薯淀粉在接枝前和接枝后的结构和性能。最佳反应条件为:丙烯酸/丙烯酰胺质量比1∶3,引发剂过硫酸钾用量是单体质量的0.125%,交联剂N,N′-亚甲基双丙烯酰胺的用量为单体质量的0.167%,反应温度为70℃,反应时间为4 h。With potassium persulphate as the initiator,a superaborbent polymer is prepared from graft copolymer of maniocca(cassava starch) with acrylic acid and acrylamide.The influences of the dosage ratio of acrylic acid with acrylamide,the reaction temperature and the amount of initiator on the absorption performance are studied,and the structure and performance of cassava starch before and after the graft are analyzed.The optimal reaction conditions are obtained as follows:weight ratio of acrylic acid to acrylami...

关 键 词：木薯淀粉 丙烯酰胺 丙烯酸 高吸水性树脂 