Preparation and Properties of Plywood Adhesives with Soy Protein Isolate Modified by SDS  

作　　者：Li Na Xie Jianjun Zeng Nian Ding Chu Ran Delong 

机构地区：[1]School of Materials Science and Engineering,Central South University of Forestry & Technology

出　　处：《Chinese Forestry Science and Technology》2012年第3期72-73,共2页中国林业科技（英文版）

摘　　要：The effects of mass concentration,the reaction temperature and the reaction time of soy protein isolate(SPI) and sodium dodecyl sulfate (SDS) on the adhesive strength of the modified SPI adhesives has been studied through orthogonal experiments.And the adhesive mechanism of the modified SPI adhesives was discussed.The results show that the optimum formula conditions are as follows:mass concentration of SPI was 14%,that of SDS 1%,reaction temperature 35℃and the reaction time 3 h.Under the optimum conditions, the dry adhesive strength of the modified SPI adhesives was 1.82 MPa,the wet adhesive strength was 0.82 MPa,the viscosity was 5.8 Pa·s,the solid content was 12.96%.After SDS was added into SPI, the composites of SDS-SPI were formed,the internal hydrophobic groups among the SPI molecule structure were turned out and the water resistance of the modified SPI adhesives was enhanced with an increase of the modification time.When the concentration of SDS was over a defined value,the disulfide bond was broken and the modification effect of SDS went bad.The effects of mass concentration,the reaction temperature and the reaction time of soy protein isolate(SPI) and sodium dodecyl sulfate (SDS) on the adhesive strength of the modified SPI adhesives has been studied through orthogonal experiments.And the adhesive mechanism of the modified SPI adhesives was discussed.The results show that the optimum formula conditions are as follows:mass concentration of SPI was 14%,that of SDS 1%,reaction temperature 35℃and the reaction time 3 h.Under the optimum conditions, the dry adhesive strength of the modified SPI adhesives was 1.82 MPa,the wet adhesive strength was 0.82 MPa,the viscosity was 5.8 Pa·s,the solid content was 12.96%.After SDS was added into SPI, the composites of SDS-SPI were formed,the internal hydrophobic groups among the SPI molecule structure were turned out and the water resistance of the modified SPI adhesives was enhanced with an increase of the modification time.When the concentration of SDS was over a defined value,the disulfide bond was broken and the modification effect of SDS went bad.

关 键 词：ADHESIVE SOY protein ISOLATE SODIUM dodecyl SULFATE ADHESIVE strength water resistance 

分 类 号：S7[农业科学—林学]