以吡啶为原料制备氮掺杂碳纳米管  

The Preparation of Nitrogen-doped Carbon Nanotubes from Pyridine

作　　者：朱素冰[1,2] 孙思修[3] 周薇薇[1] 许军舰[1] 李彦[1] 

机构地区：[1]北京大学化学与分子工程学院 [2]山东大学化学化工学院,济南250100 [3]山东大学化学化工学院

出　　处：《物理化学学报》2004年第11期1320-1323,共4页Acta Physico-Chimica Sinica

基　　金：国家自然科学基金(90101015);国家重点基础研究发展规划(973)(2001CB610503)资助项目~~

摘　　要：在700～800℃,以吡啶为原料用CVD方法制备出了管径在20～40nm的竹节状碳纳米管.EDX和结果都表明氮掺杂到碳纳米管中.HRTEM研究发现掺氮碳纳米管的竹节由数层石墨片弯曲而成,纳米管外石墨层逐渐消失.从Raman谱图的对照中发现,与相似条件下制备出的纯碳纳米管相比,氮掺杂碳纳米管的谱带对G谱带的相对强度增加,TGA研究发现掺杂纳米管在较低温度下即被氧化,这些结果都说明氮掺杂使纳米管的缺陷增加.Bamboo-like nanotubes with a diameter of 20 similar to 40 nm were prepared by thermal decomposition of pyridine at 700 similar to 800 degreesC. EDX and XPS measurements show that they are nitrogen-doped carbon nanotubes. It was found that the intensity of the D band in the Raman spectrum of the N-doped tubes is much higher than that of undoped tubes. It was also found by TGA that the doped tubes were oxidized at much lower temperature. These both indicate that nitrogen-doping introduces defects into the graphite sheets of the tubes. HRTEM result is in good agreement with this.

关 键 词：吡啶 CVD 氮掺杂 竹节状碳纳米管 

分 类 号：O613[理学—无机化学]