钢的表面带状组织及其引起的冷弯裂纹  

Superficial banded structure and its effects on bending flaws of low carbon steel strips

作　　者：柳得橹[1] 邵伟然[1] 孙贤文[1] 霍向东[1] 毛新平 李烈军 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083 [2]珠江钢铁公司,广州510730

出　　处：《北京科技大学学报》2005年第1期40-44,共5页Journal of University of Science and Technology Beijing

基　　金：国家基础发展规划研究项目(No.G1998061500)

摘　　要：分析在热轧低碳含锰钢板上观察到的表面带状组织,讨论了带状组织形成的原因和预防方法.实验测定了厚度为8mm与5mm热轧钢板冷弯时表面的局部相对伸长,通过实验结果说明表面带状组织是导致钢板出现冷弯裂纹的主要原因之一.提出了防止带状组织生成、避免冷弯裂纹的方法要点.Superficial banded structure was observed on hot strips of low carbon steel. The formation mechanism of the banded structure was discussed and some measures were proposed to minimize the superficial flows. Experiments were carried out on the surface local elongation of cold bending specimens with 8 mm and 5 mm in thickness respectively. The results indicated that the bending flaws of thick strips arise mainly from the existing of the superficial banded structure.

关 键 词：表面带状组织 成分偏聚 冷弯裂纹 低碳含锰钢 