热压工艺对竹材加工剩余物制备重组复合板性能影响的研究  

Influence of Hot-Pressing Technology on Performances of Prepare Recombine Composite Plate Processed with Bamboo Surplus Materials of Processing

作　　者：贺磊[1] 郑淼松[2] 王玉[1] 王伟[3] 高克文[1] 

机构地区：[1]江西省林业科学院,江西南昌330032 [2]连云港市林业局,江苏连云港222003 [3]徐州出入境检验检疫局,江苏徐州221006

出　　处：《江西林业科技》2011年第1期32-34,48,共4页Jiangxi Forestry Science and Technology

基　　金：江西省财政厅重大专项"竹材高效利用关键技术研究与示范"(项目编号200601)

摘　　要：采用正交实验法,研究热压工艺对竹材加工剩余物制备重组复合板性能的影响。研究结果表明:热压温度对试验结果的影响最为显著,其次是热压压力,而热压时间对试验结果的影响不明显;综合考虑产品成本及生产效率,确定最佳热压工艺为热压温度140℃、热压压力5.5 MPa、热压时间1.0 min/mm;由此工艺压制的板材,其性能能够满足汽车车厢底板及混凝土模板的要求,应用前景非常广阔。The influence of hot-pressing technology on performances of prepare recombine composite plate processed with bamboo surplus materials of processing by means of orthogonal test was studied.The results showed that:the hot-pressing temperature has the most influential effect,the following is hot pressure,but hot-pressing time has little effect.Considering of the product quality and the producing cost,the optimum process of hot-pressing is:hot-pressing temperature 140 ℃,hot pressure 5.5 MPa,the hot-pressing tim...

关 键 词：正交实验法 热压工艺 竹材加工剩余物 

分 类 号：TS653[轻工技术与工程]