无皂乳液VAC/DMC/VHE-水泥基复合材料的性能研究  

Study on Performance of VAC/DMC/VHE Soap- Free Emulstion Copolymerization- Cement Based Composite

作　　者：张学旭[1,2] 施强[3] 耿兵[3] 张书香[3] 许仲梓[1] 

机构地区：[1]南京工业大学材料学院 [2]济南大学材料学院,济南250002 [3]济南大学化学化工学院

出　　处：《硅酸盐通报》2005年第4期49-51,57,共4页Bulletin of the Chinese Ceramic Society

基　　金：国家自然科学基金资助项目(50173010)

摘　　要：研究了无皂乳液醋酸乙烯酯(VAC)/甲基丙烯酰氧乙基三甲基氯化铵(DMC)/乙烯基羟丁基醚与水泥共混所形成的水泥基复合材料的性能。研究发现,聚灰比为5%或10%时,该复合材料的抗折强度都有相应的提高,而抗压强度变化不大。与较早研究的2种无皂乳液与水泥共混所形成的复合材料比较,有更好的性能。Cement mortar was modified with soap - free emulsion VAC （vinylacetic acid）/DMC （methacyloy loxyethyl trimethylammohium chloride）/VHE （vinyl - 4 - hydrobutyl - ether） copolymerization. The effect of VAC/DMC/VHE on the strength of cement mortar was studied. The results show that soap- free emulsion VAC/DMC/VHE significantly improves bending strength of hardened cement mortar and there is a small change in their compression strength. It has better performance than that of the previously developed composite.

关 键 词：复合材料 乳液固含量 无皂乳液醋酸乙烯酯 甲基丙烯酰氧乙基三甲基氯化铵 乙烯基羟丁基醚 水泥 抗折强度 抗压强度 

分 类 号：TB332[一般工业技术—材料科学与工程]