电结晶制Co/Pt多层膜的结构及磁性研究  

Structure and Magnetic Properties of Electrodeposited Co/Pt Multilayers

作　　者：印仁和[1] 曾绍海[1] 曹为民[1] 董晓明[1] 

机构地区：[1]上海大学理学院化学系,上海200444

出　　处：《化学学报》2005年第20期1871-1874,共4页Acta Chimica Sinica

基　　金：国家自然科学基金(No.20271032);上海市教委青年基金(No.02AQ83)资助项目.

摘　　要：以单晶Si(111)为基底,在以P盐[主要成分Pt(NO2)2(NH3)2]和CoSO4为主盐的硼酸体系中电结晶Co/Pt多层膜.SEM观察多层膜的断面形貌,证实多层膜具有周期结构.经XRD测试,首次证实了Co-Pt界面上有CoPt3化合物的存在.用PPMS测试了多层膜的磁滞回线,平行于外磁场时膜的矫顽力约为165Oe,垂直于外磁场时的矫顽力随Co含量的增加而增加,最大达到396Oe.首次用电结晶方法制得了易磁化轴垂直于膜面的Co/Pt多层膜.The Co/Pt multilayers film was deposited on monocrystal Si（111） using electrocrystallization in boric acid system, in which Pt（NO2）2（NH3）2 and COSO4 were used as main salts. The cross section morphology of the multilayers was characterized by SEM method. The results showed that a periodically layered structure was obtained by electrodeposition. In Co/Pt interface, CoPt3 was found by middle angle X-ray diffraction method. The hysteresis loop of the multilayers was determined by PPMS method. The result showed that the coercivity of multilayers was about 165 Oe parallelly, and the coercivity in perpendicular increased with the content of Co, 396 Oe at a maximun. The Co/Pt multilayer with the easy-magnetization axis perpendicular to the face of layers was firstly prepared by electrocrystallization method.

关 键 词：电化学结晶 多层膜 X射线衍射 磁滞回线 垂直磁各向异性 Co/Pt多层膜 周期结构 电结晶 磁性研究 SI(111) 

分 类 号：O484.1[理学—固体物理]