高性能铌酸钾钠无铅压电陶瓷研制  

Preparation of Sodium-potassium Niobate Lead-free Piezoelectric Ceramics with High Performances

作　　者：臧国忠[1] 王矜奉[1] 明保全[1] 亓鹏[1] 杜鹃[1] 郑立梅[1] 盖志刚[1] 

机构地区：[1]山东大学物理与微电子学院,山东济南250100

出　　处：《电子元件与材料》2005年第11期27-29,共3页Electronic Components And Materials

基　　金：山东省自然科学基金资助项目(Z2003F04)

摘　　要：用常规氧化物固溶方法制备了无铅压电铌酸盐((Na0.5K0.5)1-xLixSbyNb1-yO3)陶瓷。实验结果表明,Li+和Sb5+的引入提高了陶瓷的压电性能。在一定配比范围内(Li和Sb在10%摩尔分数以内),材料为斜方、四方相共存的钙钛矿结构,材料的压电常数d33在270 pC/N以上,机电耦合系数kp、kt、k33分别达到49×10–2、43×10–2、64×10–2。介质损耗tgδ小于2.0×10_2,居里温度tC高达375℃。Sodium-potassium Niobate ceramics were prepared by conventional oxide solid-solution technique. The piezoelectric properties of Sodium-potassium Niobate at morphotropic phase boundary （MPB） were investigated, The results show that Li^＋ and Sb^5＋ could enhance the piezoelectric properties of the ceramics, which piezoelectric constant d33 is up to 270 pC/N or more, electromechanic coupling factors kp is 0.49, kt is 0.43, k33 is 0.64, dielectric loss tgδ 〈 2.0×10^-2 and curie temperature tc is up to 375℃,

关 键 词：无机非金属材料 无铅压电陶瓷 铌酸盐 机电耦合系数 居里温度 

分 类 号：TM22[一般工业技术—材料科学与工程]