Evolution of Sm2Fel7 Alloys during Hydrogenation-Disproportion Process  

作　　者：叶金文 刘颖 李梦 高升吉 涂铭旌 

机构地区：[1]Department of Metal Materials, Sichuan University, Chengdu 610065, China

出　　处：《Journal of Rare Earths》2005年第5期542-545,共4页稀土学报（英文版）

摘　　要：The evolution of phase compositions, phase change and microstructure in Sm2Fe17 alloys during hydrogenationdisproportion process were systematically studied with XRD, SEM, EDX methods. Research indicates that HD process of Sm2Fe17 alloys is as follows： Sm2Fe17 alloy absorbs hydrogen first in the atmosphere of hydrogenation with a pressure of 0.1 MPa. Disproportionation begins at T ≥ 500 ℃, then the alloys tuna into lots of SmHx and α-Fe phases which are partly in microcrystal or amorphous structures. Along with the increase of temperature, the microcrystal and amorphous structures transformed into crystal structure and this transformation thoroughly completed at 750 ℃. The size of obtained crystal grain is about 20 - 100 nm. Based on the experimental data, a microstructural transformation model of Sm2Fe17 alloys during hydrogenation-disproportion process was made.The evolution of phase compositions, phase change and microstructure in Sm2Fe17 alloys during hydrogenationdisproportion process were systematically studied with XRD, SEM, EDX methods. Research indicates that HD process of Sm2Fe17 alloys is as follows： Sm2Fe17 alloy absorbs hydrogen first in the atmosphere of hydrogenation with a pressure of 0.1 MPa. Disproportionation begins at T ≥ 500 ℃, then the alloys tuna into lots of SmHx and α-Fe phases which are partly in microcrystal or amorphous structures. Along with the increase of temperature, the microcrystal and amorphous structures transformed into crystal structure and this transformation thoroughly completed at 750 ℃. The size of obtained crystal grain is about 20 - 100 nm. Based on the experimental data, a microstructural transformation model of Sm2Fe17 alloys during hydrogenation-disproportion process was made.

关 键 词：metal materials HDDR HYDROGENATION NITRIDE rare earths 

分 类 号：TM273[一般工业技术—材料科学与工程]