微米级薄片木纤维高强度人造板制造工艺的试验研究  

Study of processing MFB with wood micro-fiber

作　　者：阿伦[1] 马岩[1] 战丽[1] 许彦博[1] 杨春梅[1] 孟庆军[1] 

机构地区：[1]东北林业大学林业与木工机械工程技术中心,哈尔滨150040

出　　处：《木材加工机械》2006年第1期22-24,共3页Wood Processing Machinery

基　　金：国家自然科学基金资助项目(39870637)

摘　　要：利用微米级长木纤维在实验室成功地压制了人造板,初步验证了微米级木纤维形成高强度纤维板(MFB)的细胞裂解理论。试验结果表明这种板材外观呈现木本色,在某些物理力学性能上(MOR,MOE,握钉力等)优于MDF和B类刨花板。This paper focused on a new wood-based panel---MFB, which was pressed with wood micro-fiber, proved the cell break theory of using wood fiber micro-meter reconsolidated technology forming super high-strength wood-based panel successfully in the laboratory, and also made a comparison of physical and mechanical properties among particleboard of kind B, MDF, OSB, HDF, and MFB. The results showed that MFB is in wooden color and high strength.

关 键 词：微米 木纤维 MEB 试验 

分 类 号：TS653[轻工技术与工程]