溶胶-凝胶法制备ZnO薄膜的成核-生长和失稳分解研究  

Nucleation-growth and spinodal decomposition of zinc oxide films prepared by sol-gel technique

作　　者：臧竞存[1] 田战魁[1] 刘燕行[2] 迟静[1] 邹玉林[1] 魏建忠[1] 叶建萍[3] 

机构地区：[1]北京工业大学材料科学与工程学院,北京100022 [2]北京工业大学环境与能源工程学院,北京100022 [3]中国科学院化学研究所光化学重点实验室,北京100080

出　　处：《物理学报》2006年第3期1358-1362,共5页Acta Physica Sinica

基　　金：中国科学院化学研究所光化学开放实验室基金资助的课题.~~

摘　　要：采用溶胶-凝胶法在ZnWO4单晶上制备出透明的ZnO薄膜.通过光学显微镜观察了ZnO薄膜的表面形貌.实验结果表明,ZnO薄膜的形成经历了表面成核,晶粒长大和岛的形成三个不同的阶段.由于ZnO晶核是在非平衡条件下生长的,在生长过程中不可避免地出现了枝晶生长和分形生长以及失稳分解.Transparent zinc oxide （ZnO） films were prepared on ZnWO4 crystal by sol-gel technique. Surface morphology of ZnO films were observed with optical microscope. The results of show that ZnO films are formed in three different stages from nucleation on surface, grain growth to island formation. Because ZnO crystal nucleus were grown under non-equilibrium condition, it is inevitable that dendrite growth, fractal growth and spinodal decomposition phenomenon are involved in the growing process.

关 键 词：氧化锌薄膜 成核 枝晶生长 分形生长 失稳分解 