Al_2O_3／WC-Co金属陶瓷的制备与性能研究  

Preparation and Properties of Al_2O_3/WC-Co Cermet

作　　者：熊震[1] 邵刚勤[1] 段兴龙[1] 史晓亮[1] 

机构地区：[1]武汉理工大学材料复合新技术国家重点实验室,湖北武汉430070

出　　处：《稀有金属材料与工程》2006年第A02期79-82,共4页Rare Metal Materials and Engineering

基　　金：国家"863"纳米材料专项(2002AA302504);武汉市科技攻关(20041003068-04);武汉理工大学科技基金(2003XJJ005;2003XJJ200)

摘　　要：以亚微米Al2O3粉末和WC-Co粉末为原料,经热压烧结制备了Al2O3/WC-Co金属陶瓷。用XRD、SEM测试了物相组成和显微结构,用VSM测试了磁滞回线。获得了断裂韧性为6．042 MPa·m1/2、洛氏硬度为92．0 HRA的金属陶瓷。Al2O3/WC-Co cermets were prepared by a hot-pressing process. Its phase composition and microstructure were investigated by means of X-ray diffraction （XRD） and scanning electron microscopy （SEM） analysis. The hysteresis loops was measured with VSM. Its fracture toughness and Rockwell hardness were tested by single edged notch beam （SENB） and indentation technique. The sintered sample exhibits a hardness with 92.0 HRA and fracture toughness with 6.042 MPa·m^1/2.

关 键 词：金属陶瓷 AL2O3 WC-CO 力学性能 

分 类 号：TG148[一般工业技术—材料科学与工程]