锑红宝石玻璃的研制与探讨  

Research and Discussion on the Antimony Ruby Glass

作　　者：孙成果[1] 宁伟[1] 汪庆卫[1] 

机构地区：[1]东华大学材料科学与工程学院,上海200051

出　　处：《玻璃与搪瓷》2007年第2期10-14,共5页Glass & Enamel

摘　　要：在Na2O-CaO-SiO2玻璃系统中引入着色剂,熔制锑红玻璃试样,讨论不同着色剂的用量、不同退火时间对试样透过率的影响。结果表明:锑红玻璃的截止波长随着着色剂的增加和热处理时间的延长而向长波移动,其透过曲线与硒红玻璃接近,但是吸收带比较宽,其各种性能与硒红玻璃的性能比较接近。The antimony ruby glass samples based on Na2O-CaO-SiO2 glass system ana doped with colorant were obtained. Effects of dosage of the colorant and heat treatment on transmission of the glass were investigated. The results showed that the cut-off wavelength of the antimony ruby glass moved to long wave with the increase of the colorant and the heat treatment time. Its transmission curve was similar to the selenium ruby glass, but its absorption band was wider, the performances of these antimony glasses were very close to the selenium ruby glasses

关 键 词：锑红玻璃 透过光谱曲线 着色剂 热处理 

分 类 号：TQ171.734[化学工程—玻璃工业]