热处理参数对中碳低合金铸钢组织与力学性能的影响  

The influence of Heat treatment Parameters to the Microstructure and Mechanical Properties of Medium Carbon Low Alloy As-steel

作　　者：黄志求[1] 

机构地区：[1]佳木斯大学材料科学与工程学院,黑龙江佳木斯154007

出　　处：《佳木斯大学学报（自然科学版）》2007年第2期187-188,共2页Journal of Jiamusi University：Natural Science Edition

基　　金：黑龙江省教育厅科学技术研究资助项目(11511385);佳木斯大学科学技术研究资助项目(L33)

摘　　要：研究了奥氏体化温度、等温淬火工艺参数对化学成分（wt%）为0.40%C,1.2%Si,1.1%Mn,0.9%Cr中碳低合金铸钢力学性能的影响.光学显微组织、冲击韧性测试结果表明,试样在340-380℃范围内经等温淬火处理后,可以获得无碳化物析出的奥氏体-贝氏体组织,且随着等温淬火温度的升高,贝氏体形貌由板条状下贝氏体逐渐向上贝氏体转变,试样的硬度达到HRC44,冲击韧性ak≥120J/cm^2.Influence of austempering heat treatment parameters on the mechanical properties of cast steel（chemical composition is 0.40%C,1.2%Si,1.1% Mn, 0.9% Cr ,all in wt%） was investigation. LOM, TEM and XRD were adopted to analyze structure, The tests result showed specimens obtained austenite - bainite microstructure without carbide appeared after austempering technology rang from 340℃ to 380℃ quenching. With isothermal quenching temperature increasing the microstructure shape of specimens changed from lathing lower bainite to upper bainite. The hardness was HRCA4, and toughness was more than 120J/cm^2.

关 键 词：奥氏体化温度 等温淬火工艺 奥氏体-贝氏体 力学性能 

分 类 号：TG162[金属学及工艺—热处理]