采用PITT与EIS技术测定锂离子电池正极材料LiFePO_4中锂离子扩散系数  

Measurement of diffusion coefficient of lithium in LiFePO_4 cathode material for Li-ion battery by PITT and EIS

作　　者：曲涛[1] 田彦文[2] 翟玉春[2] 

机构地区：[1]中山大学物理科学与工程技术学院 [2]东北大学材料与冶金学院,沈阳110004

出　　处：《中国有色金属学报》2007年第8期1255-1259,共5页The Chinese Journal of Nonferrous Metals

基　　金：辽宁省科技厅攻关资助项目(2003224005)

摘　　要：采用恒电位间歇滴定法(PITT)和电化学阻抗谱技术(EIS)测定锂离子电池正极材料LiFePO4中Li+扩散系数。结果表明:随着嵌锂量的变化,锂离子的扩散系数(D Li+)先出现一个极大值,然后出现一个极小值,随后随嵌锂量的增加而增大;扩散系数在10-13 cm2/s^10-16 cm2/s数量级范围内变化;2种方法计算得到的扩散系数在数量级上相符合。The chemical diffusion coefficient of Li-ion in LiFePO4 cathode material was measured by potentiostatic intermittent titration technique （PITT） and electrochemical impedance spectrum （EIS）. The results show that the diffusion coefficient ranges in 10^-13-10^-16 cm^2/s. With the change of Li content the diffusion coefficient appears an extremely large value firstly, latter appears a minimum, then increases. The calculated values by PITT are in agreement with those by EIS.

关 键 词：LIFEPO4 扩散系数 PITT EIS 