Preparation and Luminescence Characteristics of Ca3Y2（BO3）4：Eu^3＋ Phosphor  

作　　者：李盼来 杨志平 王志军 郭庆林 

机构地区：[1]College of Physics Science and Technology, Hebei University, Baoding 071002

出　　处：《Chinese Physics Letters》2007年第10期2977-2979,共3页中国物理快报（英文版）

摘　　要：Ca3Y2 （BO3）4：Eu^3＋ phosphor is synthesized by high temperature solid-state reaction method, and the Iuminescence characteristics are investigated. The emission spectrum exhibits two strong red emissions at 613 and 621 nm corresponding to the electric dipole ^5 Do- ^7F2 transition of Eu^3＋ under 365 nm excitation, the reason is that Eu^3＋ substituting for Y^3＋ occupies the non-centrosymmetric position in the crystal structure of Ca3 Y2 （BO3）4. The excitation spectrum for 613 nm indicates that the phosphor can be effectively excited by ultraviolet （UV） （254 nm, 365nm and 400nm） and blue （470nm） light. The effect of Eu^3＋ concentration on the emission intensity of Ca3 Y2 （BO3）4 ：Eu^3＋ phosphor is measured, the result shows that the emission intensities increase with increasing Eu^3＋ concentration, then decrease. The CIE colour coordinates of Ca3Y2 （BO3）4：Eu^3＋ phosphor is （0.639, 0.357） at 15mol% Eu^3＋.Ca3Y2 （BO3）4：Eu^3＋ phosphor is synthesized by high temperature solid-state reaction method, and the Iuminescence characteristics are investigated. The emission spectrum exhibits two strong red emissions at 613 and 621 nm corresponding to the electric dipole ^5 Do- ^7F2 transition of Eu^3＋ under 365 nm excitation, the reason is that Eu^3＋ substituting for Y^3＋ occupies the non-centrosymmetric position in the crystal structure of Ca3 Y2 （BO3）4. The excitation spectrum for 613 nm indicates that the phosphor can be effectively excited by ultraviolet （UV） （254 nm, 365nm and 400nm） and blue （470nm） light. The effect of Eu^3＋ concentration on the emission intensity of Ca3 Y2 （BO3）4 ：Eu^3＋ phosphor is measured, the result shows that the emission intensities increase with increasing Eu^3＋ concentration, then decrease. The CIE colour coordinates of Ca3Y2 （BO3）4：Eu^3＋ phosphor is （0.639, 0.357） at 15mol% Eu^3＋.

关 键 词：LIGHT-EMITTING-DIODES 

分 类 号：O43[机械工程—光学工程]