退火对稀土系AB5低钴贮氢合金性能的影响  

Effects of annealing treatment on the properties of rare earth-based AB5 low-Co hydrogen storage alloy

作　　者：李全安[1] 蔚如意[1] 谢封超 程树国 

机构地区：[1]河南科技大学材料科学与工程学院,河南洛阳471003 [2]河南环宇集团,河南新乡453000

出　　处：《功能材料》2007年第A04期1599-1601,共3页Journal of Functional Materials

基　　金：基金项目：河南省杰出青年科学基金资助项目（0312000200）;河南省高校创新人才培养基金资助项目（豫高教（200210129）

摘　　要：研究了600与900℃两种温度退火对低钴贮氢合金MI（NiMnAlCuFeSnZn）4.7CO0.3的微观结构、组织以及电化学性能的影响。XRD分析表明退火降低了合金的晶格应力和缺陷，同时使得合金的单胞体积增大。电化学测试结果表明，退火处理后合金的放电容量有所提高，循环稳定性有所改善。The effects of 600 and 900℃ annealing treatments on the phase structure, microstructures and electrochemical properties of low-Co MI（NiMnA1CuFeSnZn）4.7CO0.3 hydrogen storage alloys were investigated. The results of XRD analyses indicated that annealing treatment reduced the lattices train and defects of the as-cast alloy, and improved the unit-cell volume. The electrochemical tests indicated that the annealed alloys, as compared with as-cast alloy, showed a higher discharge capacity, better cycling stability.

关 键 词：低钴贮氢合金 退火 MH Ni电池 