中温黑色磷化膜的研究  

Reserch on the Black Phosphating Film at the Mid-temperature

作　　者：王建胜[1] 刘力拓 

机构地区：[1]中国嘉陵集团,重庆400032 [2]西安航天化学动力厂,陕西西安710025

出　　处：《表面技术》2008年第1期64-66,共3页Surface Technology

摘　　要：为了研究一种中温黑色磷化工艺,借助金相显微镜和扫描电镜对磷化膜的结构和形貌进行表征。黑色磷化膜表调后的厚度为6μm,其厚度为表调前传统磷化膜的1/3左右。通过表调也可使磷化膜均匀、致密,耐蚀性得到明显提高。硫酸铜点滴腐蚀时间是国家标准的4倍,氯化钠浸渍达72h。结果得到了一种成本低廉、无沉渣、无毒、膜黑的工业生产型磷化液。此工艺可以满足工业化批量生产要求。A black phosphating process at mid-temperaturem was discussed. The morphology and structure of the phosphating film were analyzed by means of the gold mutually microscope and SEM. The thickness of the black phosphating coating can reach to 6μm by surface conditioning process, which is nearly one third the thickness of the traditional phosphating coating without surface conditioning process. And it shows that the compact and continuity, corrosion resistance of the film will be improved obviously by surface conditioning process. The corrossion time in copper sulfate spot test is four times as high as national standard and the time for sodium chloride bath test is up to 72h. It was found out that the obtained black phosphating film is low cost, no-sedimented, nonpoisonous, and can make the production of phosphating bath industrialized. The technics can meet the requirements of the industrialized mass production.

关 键 词：磷化处理 中温 黑色 金相显微镜 SEM 发黑工艺 

分 类 号：TG178[金属学及工艺—金属表面处理]