纯铜表面Fe-Al共渗组织结构及性能研究  

Study on the structure and property of iron-aluminum diffusing layer on pure copper substrate

作　　者：王国凡[1] 汤爱君[1] 罗辉[1] 苗磊[1] 

机构地区：[1]山东建筑大学材料科学与工程学院,山东济南250101

出　　处：《山东建筑大学学报》2008年第1期54-57,共4页Journal of Shandong Jianzhu University

基　　金：山东省科学自然基金资助项目(Y2005F18)

摘　　要：利用固体粉末法在纯铜表面进行Fe-Al共渗,借助扫描电镜、X射线衍射仪和显微硬度计,分别测定渗层的组织结构及表面硬度,并对共渗前后纯铜表面耐磨及高温抗氧化性能进行了对比实验。研究结果表明,Fe和Al在紫铜基体中以固溶体形式存在,形成的含铝α+(α+γ2)组织提高了铜的表面硬度及高温抗氧化性能,而Fe作为形核核心有可能起到细化α+γ2组织的作用,α+γ2片间距减小可使表面耐磨性能相应提高。By using the solid powder method, the iron-aluminum diffusing layer experiments were done on pure copper substrate. With the scanning electron microscope, X-ray diffraction instrument and micro-hardness instrument, this paper tests the structure and the surface hardness of diffusing layer were tested respectively. Mso, the wearing resistance and high-temperature oxidation resistance experiments were made on pure copper substrate fore-and-aft the diffusing, respectively. The results showed that iron and aluminum could dissolve in copper substrate, the α ＋ （α ＋ γ2 ）structure including aluminum could increase the surface hardness and high- temperature oxidation resistance, and, as the core of shape, iron might thin α ＋ γ2 structure, the decreased ＋ γ2 layer distant could improve the surface wearing resistance.

关 键 词：Fe-Al共渗 纯铜 耐磨性 抗氧化性 

分 类 号：TG156.8[金属学及工艺—热处理]