Effects of Solution Treatment Time and Sr-Modification on Microstructure and Mechanical Property of Al-Si Piston Alloy  

作　　者：Witthaya Eidhed 

机构地区：[1]Department of Production Technology Faculty of Engineering,King Mongkut's Institute of Technology North Bangkok,10800,Thailand

出　　处：《Journal of Materials Science & Technology》2008年第1期29-32,共4页材料科学技术（英文版）

摘　　要：The purpose of this paper was to investigate the effects of solution treatment time and Sr-modification on the microstructure and property of the Al-Si piston alloy.It was found that as-cast microstructures of unmodified and Sr-modified Al-Si alloys consisted of a coarse acicular plate of eutectic Si,Cu_3NiAl_6 and Mg_2Si phases in theα-Al matrix but different in size and morphology.Both size and inter-particle spacing of Si particles were significantly changed by increasing the solution treatment time.After a short solution treatment,the coarse acicular plate of the eutectic Si appears to be fragmented.Fully modified microstructure of Sr-modified alloy can reduce the solution treatment time compared to unmodified alloy.The maximum of a peak hardness value is found in the very short solution treatment of both Al-Si piston alloys.Compared to 10 h solution treatment,the solution treatment of 2-4 h is sufficient to achieve appropriate microstructures and hardness. The short solution treatment is very useful to increase the productivity and to reduce the manufacturing cost of the Al-Si piston alloys.The purpose of this paper was to investigate the effects of solution treatment time and Sr-modification on the microstructure and property of the Al-Si piston alloy.It was found that as-cast microstructures of unmodified and Sr-modified Al-Si alloys consisted of a coarse acicular plate of eutectic Si,Cu_3NiAl_6 and Mg_2Si phases in theα-Al matrix but different in size and morphology.Both size and inter-particle spacing of Si particles were significantly changed by increasing the solution treatment time.After a short solution treatment,the coarse acicular plate of the eutectic Si appears to be fragmented.Fully modified microstructure of Sr-modified alloy can reduce the solution treatment time compared to unmodified alloy.The maximum of a peak hardness value is found in the very short solution treatment of both Al-Si piston alloys.Compared to 10 h solution treatment,the solution treatment of 2-4 h is sufficient to achieve appropriate microstructures and hardness. The short solution treatment is very useful to increase the productivity and to reduce the manufacturing cost of the Al-Si piston alloys.

关 键 词：Al-Si based alloy Solution treatment Sr-modification AGE-HARDENING 

分 类 号：TG146.21[一般工业技术—材料科学与工程]