Influence of binder composition on the rheological behavior of injection-molded microsized SiC suspensions  

作　　者：Islam S.Humail 

机构地区：[1]School of Materials Science and Engineering,University of Science and Technology Beijing

出　　处：《Journal of University of Science and Technology Beijing》2008年第3期297-301,共5页北京科技大学学报（英文版）

基　　金：the National Natural Science Foundation of China(No.50274014)

摘　　要：The influence of four kinds of binders consisting of paraffin wax （PW）, random-polypropylene （RPP）, high-density polyethylene （HDPE）, and stearic acid （SA） on the theological behavior of injection-molded SiC feedstocks was investigated over a temperature range of 150℃ to 180℃ and a shear rate range of 4 s^-1 to 1259 s^^-1. The results showed that all the feedstocks exhibited pseudoplastic flow behavior. The wax-based binder of multipolymer components （PW-RPP-HDPE） exhibited better comprehensive rheological properties compared with the binder of monopolymer components （PW-RPP or PW-HDPE）. The addition of 5wt% SA to the binder could reduce the viscosity of the feedstock but enhance the rheological stability by improving the wettability between the binder and the SiC powder. The binder of 65wt% PW ＋ 15wt% HDPE ＋ 15wt% RPP ＋ 5wt% SA was found to be a better binder for microsized SiC injection molding.The influence of four kinds of binders consisting of paraffin wax （PW）, random-polypropylene （RPP）, high-density polyethylene （HDPE）, and stearic acid （SA） on the theological behavior of injection-molded SiC feedstocks was investigated over a temperature range of 150℃ to 180℃ and a shear rate range of 4 s^-1 to 1259 s^^-1. The results showed that all the feedstocks exhibited pseudoplastic flow behavior. The wax-based binder of multipolymer components （PW-RPP-HDPE） exhibited better comprehensive rheological properties compared with the binder of monopolymer components （PW-RPP or PW-HDPE）. The addition of 5wt% SA to the binder could reduce the viscosity of the feedstock but enhance the rheological stability by improving the wettability between the binder and the SiC powder. The binder of 65wt% PW ＋ 15wt% HDPE ＋ 15wt% RPP ＋ 5wt% SA was found to be a better binder for microsized SiC injection molding.

关 键 词：SIC powder injection molding RHEOLOGY BINDER 

分 类 号：TQ320.662[化学工程—合成树脂塑料工业]