十二烷基二硫代三嗪的合成及摩擦学性能研究  

SYNTHESIS AND TRIBOLOGICAL BEHAVIOUR OF TRIAZINE DERIVATIVE AS ADDITIVE OF RAPESEED OIL

作　　者：范成凯[1] 李芬芳[1] 周茂林[1] 

机构地区：[1]中南大学化学化工学院,长沙410083

出　　处：《石油炼制与化工》2008年第11期35-38,共4页Petroleum Processing and Petrochemicals

基　　金：中国人民解放军总后勤部军需物资油料部资助项目(需物油科[2006]357号);湖南省科技计划项目(06FJ4112)

摘　　要：合成了一种新型无灰、无磷三嗪衍生物十二烷基二硫代三嗪(TOBT)。以菜籽油作为基础油,采用 MRS-10A 型四球摩擦磨损试验机考察了其摩擦学性能,分析了载荷、摩擦时间、添加剂添加量对菜籽油摩擦学性能的影响。结果表明,该添加剂能大幅度提高菜籽油的抗磨减摩性能和承载能力,是一种性能良好的润滑油添加剂。与二硫化十二烷(TOTT)的摩擦学性能相比,TOBT 的抗磨减摩作用更为突出,说明硫含量较高、分子内存在致密三嗪杂环的添加剂具有更好的摩擦学性能。A new ashless and non-phosphorus containing triazine derivative, 2, 4, 6-tri（n- dodecyldithio）-1, 3,5-s-triazine（TOBT）, was prepared. Using rapeseed oil（RSO）as base oil, the effects of load,testing time and additive dosage on the tribological performance of RSO with and without additives were investigated by a four-ball test machine. Results showed that TOBT used as additive of RSO exhibited good anti wear and friction reducing properties, as well as enhanced load-carrying capacity. The friction coefficient of RSO having TOBT was lower as compared with that of RSO. The tribological performance of RSO having TOBT was better than that of RSO having dithiododecyl（TOTT）additive, which indicated that the higher sulfur content and the existence of compact triazine structure in TOBT could effectively improve its tribological performance as additive.

关 键 词：三嗪 菜籽油 摩擦学性能 

分 类 号：TE624.82[石油与天然气工程—油气加工工程] TH117.22[机械工程—机械设计及理论]