镍铬合金烤瓷冠冠组织面离子析出的研究  

The study of ion educed from oxide film of fired Ni-Cr porcelain alloy crowns in artificial saliva

作　　者：张荣和[1] 宋琦[2] 张勇[2] 

机构地区：[1]滨州医学院附属口腔医院口腔修复科,山东滨州256600 [2]遵义医学院附属口腔医院口腔修复科,贵州遵义563003

出　　处：《国际口腔医学杂志》2008年第6期611-614,共4页International Journal of Stomatology

摘　　要：目的研究含铬质量分数不同的两种镍铬合金烤瓷冠在人工唾液中镍、铬离子的析出量。方法用含铬质量分数为26.0%和12.6%的镍铬烤瓷合金,烧结成各12颗烤瓷冠,分别放于人工唾液中,于1、2、4、8、16、32周末用石墨炉原子吸收分光光度计测量各样本在人工唾液中的镍、铬离子浓度。结果1）低铬和高铬合金冠组样本中铬离子析出量从1～4周逐渐增加,然后逐渐下降;高铬合金冠组镍离子析出于第4周达到高峰,而低铬合金冠组镍离子的析出呈持续缓慢地上升;2）实验前后低铬合金冠组烤瓷冠的质量差别大于高铬合金冠组,其差异有统计学意义（P〈0.01）。结论1）低铬和高铬合金冠组铬离子的析出量均于第4周达高峰;2）低铬合金冠组镍离子的析出明显高于高铬合金冠组;3）实验前后低铬合金冠组样本的质量损失明显大于高铬合金冠组。Objective To study and analyze the quantity of the Ni-ion and Cr-ion educed from two types of Ni-Cr-poreelain alloy erowns in artificial saliva, to instruct clinical applications. Methods Ni-Cr porcelain alloy which contains Cr 26.0% and 12.6% were fritted into 24 Ni-Cr porcelain fused to metal crowns, and divided two groups according to Cr concentration. Both two groups included 12 ones respectively. Twenty-four samples were averagely divided into two groups. Group A： High-chromium alloy group; Group B： Low-chromium alloy group. They were put into artificial saliva in sealed eontainer. The concentration of Ni-ion and Cr-ion were measured at the first, second, fourth, eighth, sixteenth and thirty-second weekends with graphite furnaee atomie absorption spee trometry. Results 1）The educed Cr-ion from 24 samples of two groups increased slowly at the first weekend to the four week, then decreased. The edueed Ni-ion from 24 samples kept increasing from first weekend to the thirty-second weekend. 2）The mass of low-chromium porcelain alloy group decreased were more than that of high-chromium alloy group after experiment （P〈0.01）. Conclusion 1）The educed chromium ion level reached the peak at the forth weekend. 2）The educed nickel ion in the low-ehrornium alloy group was much higher than that of the high-chromium alloy group. 3）The loss of mass in low-chromium alloy group was much higher than in the high- chromium alloy group.

关 键 词：镍铬烤瓷合金 石墨炉原子吸收分析法 离子析出 金属腐蚀 

分 类 号：R783.1[医药卫生—口腔医学]