PDM-AM/纳米插层复合蒙脱石和PDM-AM-GL/纳米插层复合蒙脱石性能的对比  

PROPERTIES OF POLYMER DIALLYLDIMETHYLAMMONIUM CHLORIDE-ACRYLAMIDE/NANO INTERCALATION MONTMORILLONITE AND POLYMER DIALLYLDIMETHYLAMMONIUM CHLORIDE-ACRYLAMIDE- GLYOXAL/NANO INTERCALATION MONTMORILLONITE

作　　者：高党鸽[1] 马建中[1] 李运[1] 吕斌[1] 

机构地区：[1]陕西科技大学资源与环境学院,西安710021

出　　处：《硅酸盐学报》2008年第12期1791-1796,共6页Journal of The Chinese Ceramic Society

基　　金：国家自然科学基金(50573047);国家教育部新世纪优秀人才支持计划(NCET-04-0973);陕西科技大学科研创新团队建设(SUST-A03)资助项目

摘　　要：以单体转化率、聚合物的特性黏度和复合材料旋转黏度为指标,对聚二烯丙基二甲基氯化铵-丙烯酰胺(polymer diallyldimethylammonium chloride-acrylamide,PDM-AM)/纳米插层复合蒙脱石(montmorillonite,MMT)和聚二烯丙基二甲基氯化铵-丙烯酰胺-乙二醛(glyoxal,GL)(PDM-AM-GL)/纳米插层复合MMT分别进行了研究,并对其进行了Fourier红外光谱(Fourier transform infrared spectrometer,FTIR)分析和X射线衍射(X-ray diffraction,XRD)检测。将PDM-AM/纳米插层复合MMT和PDM-AM-GL/纳米插层复合MMT分别应用于皮革预鞣,再用质量分数为2%的标准铬粉鞣制。FTIR结果表明:单体在蒙脱石的存在下成功聚合,通过离心处理能够将聚合物与蒙脱石成功分离。XRD结果表明:PDM-AM/纳米插层复合MMT和PDM-AM-GL/纳米插层复合MMT中蒙脱石的层间距的变化规律相一致。PDM-AM/纳米插层复合MMT与GL的反应使得蒙脱石的层间距有所增加。应用结果表明:采用PDM-AM/纳米插层复合MMT预鞣不利于2%铬粉鞣制;然而当引入醛基之后,采用PDM-AM-GL/纳米插层复合MMT预鞣后,坯革的耐湿热稳定性、填充性均优于单独采用2%铬粉鞣制的坯革。The characteristics of polymer diallyldimethylammonium chloride-acrylamide/nano intercalation montmorillonite （PDMAM/MMT） and polymer diallyldimethylammonium chloride-acrylamide-glyoxal/nano intercalation montmorillonite （PDM-AM- GL/MMT） were determined by the Fourier transform infrared spectrometer, X-ray diffraction, monomer translation ratio, and characteristic viscidity of the polymer respectively. PDM-AM/MMT and PDM-AM-GL/MMT associated with 2% （in mass, the same below） chromate were applied in leather-making, and the physical-mechanical of performance of the resultant leather was measured respectively. The FTIR results show that MMT and polymer could be separated successfully by a centrifugal effect. The XRD analysis indicates that inter laminar distance of MMT in PDM-AM-GL/MMT was bigger than in PDM-AM/MMT. The application results indicate that PDM-AM/MMT associated with 2% chromate was not beneficial for leather tannage, but PDM-AM-GL/MMT associated with 2% chromate could obviously improve the shrinkage temperature, thickness increment and mechanical properties of leather.

关 键 词：蒙脱石 插层环化聚合 黏度 二烯丙基二甲基氯化铵 