InGaN蓝光与CdTe纳米晶基白光LED  

White-lighting LEDs from InGaN Blue LEDs and CdTe Nanocrystals

作　　者：易觉民[1] 李红博[2] 唐芳琼[2] 宋振阳[1] 杨志坚[2] 张国义[1] 

机构地区：[1]北京大学物理学院人工微结构与介观物理国家重点实验室,北京100871 [2]中国科学院理化技术研究所,北京100190

出　　处：《发光学报》2008年第6期1071-1075,共5页Chinese Journal of Luminescence

基　　金：国家自然科学基金(60577030,60776041);国家自然科学基金重点(60736001);国家重大基础研究“973”计划(2007CB307004)资助项目

摘　　要：报道了倒装焊InGaN蓝光LED与黄光CdTe纳米晶的复合结构。利用蓝光作为CdTe纳米晶的激发源,通过光的下转换机制,将部分蓝光转化为黄光,复合发射出白光。室温下正向驱动电流为10mA时,发光色品坐标为x=0.29,y=0.30。实验表明,该复合结构白光LED的一大优点在于,复合光的色品坐标几乎不随正向驱动电流大小变化,颜色稳定。GaN-based blue light-emitting diodes （LEDs） has been energy saving, commercial solid state lighting devices. But the research on GaN-based white-lighting LEDs has been expected to further study before commercialization. One kind of white LEDs consists of GaN-based LEDs and luminant phosphors, but conventional phosphors for GaN-based LEDs are undesirable, for example, phosphors matching GaN-based LEDs can hardly be found. Furthermore, losses caused by self-absorption or scattering of secondary photons in the phosphor medium itself contributes to a large part. In this study, CdTe nanocrystals as nanophosphor for GaNbased blue LEDs are discussed. CdTe NCs were prepared in aqueous solution employing thioglycolic acid （TGA） as stabilizer, the corresponding PL peak position of the NCs excited by 470 nm is 566 nm with full width at half maximum （FWHM） of 30 nm, indicating of monodisperse distribution. The large Stokes shift between its absorption and PL spectra would alleviate self-absorption loss. The InGaN/GaN multiple quantum wells （MQWs） epitaxial wafers were grown at （0001） plane sapphire substrate by the metalorganic chemicalvapor deposition systems （MOCVD）, and flip-chip blue LEDs were fabricated with the standard procedure, blue light from MQWs was extracted from polished sapphire plane. A hybrid structure integrating flip-chip LEDs and nanocrystals was reported. CdTe NCs were deposited directly on transparent sapphire layer, which avoids the light emitted by CdTe NCs traped in high-index GaN cavity. And another advantage of the flip-chip structure for CdTe NCs reduces the losses from quenching of the luminescence, a behavior that has been well documented with NCs attaching to smooth metallic electrodes. Blue light part from InGaN LEDs in the hybrid structure provides blue element, and also acts as a pumping resource to excite CdTe nanocrystals to emit yellow light. From photoluminescence excitation （ PLE ） spectrum of CdTe NCs and electroluminescence （EL） of GaN-based LEDs, the a

关 键 词：氮化镓 白光 发光二极管 碲化镉 纳米晶 纳米荧光粉 

分 类 号：O482.31[理学—固体物理]