模板法制备超级电容器活性炭电极材料  

Activated carbon as supercapacitor electrode material prepared by template method

作　　者：王仁清[1] 方勤[1] 邓梅根[1] 

机构地区：[1]江西财经大学电子学院,江西南昌330013

出　　处：《电子元件与材料》2009年第1期14-16,共3页Electronic Components And Materials

基　　金：江西省自然科学基金资助项目(No.2007GZS0071);江西省教育厅科技基金资助项目(No.GJJ08347)

摘　　要：以硅溶胶为模板剂,酚醛树脂为炭源,采用模板法制备了超级电容器活性炭电极材料。利用SEM和BET对实验制备的活性炭进行了分析和表征。以实验研制的活性炭为电极材料,通过循环伏安和恒流充放电测试对其电容性能进行了研究。结果表明:实验研制的活性炭的比表面积为1840m2/g,在7.5×10–3A/cm2的电流密度下,其比容达到290F/g。Activated carbon （AC） used as electrode material for supercapacitor was prepared by template method using silica sol as template and phenolics as carbon source. SEM and BET were used to analyse the as prepared AC, the AC was made into supercapacitor electrode to study its capacitive performance by cyclicvoltammogram and galvanostatic charge/discharge. The results show that the specific surface area of the AC is 1 840 m^2/g. At a current density of 7.5 × 10^-3A/cm^2, a specific capacitance of 290 F/g is reached. Supercapacitors based on the AC have low Res and excellent power property.

关 键 词：超级电容器 模板法 活性炭 比容 

分 类 号：TM911[电气工程—电力电子与电力传动] TM53