4Cr5MoSiV1钢顶杆离子渗氮技术的研究  

Study on Ion Nitriding Technology for Mould Push Rod of Steel 4Cr5MoSiV1

作　　者：邓光华[1,2] 王慧霞[1,2] 吴家亮 

机构地区：[1]福州大学材料系 [2]厦门星隆模具厂

出　　处：《金属热处理》1998年第3期9-11,共3页Heat Treatment of Metals

摘　　要：分析了４Ｃｒ５ＭｏＳｉＶ１钢模具顶杆离子渗氮技术的难点。提出设置辅助阴极改善顶杆渗氮温度均匀性的对策。根据试验结果指出，只有以热分解氨为气源采用合适的温度与气压，才能使顶杆达到均匀而有效的硬化效果。文中还讨论了顶杆离子渗氮的特性以及解决畸变问题的途径。The　difficulties　on　ion　nitriding　for　mould　push　rod　of　steel　4Cr5MoSiV1　had　been　analysed.The　method　to　set　an　assist　cathode　was　proposed　to　improve　temperature　uniformity　when　nitriding　treatment　of　the　push　rod　is　carried　out.The　experiment　results　show　that　the　uniform　and　effective　harden　effect　for　the　push　rod　can　be　reached　only　in　heat　decomposition　ammonia　and　under　proper　temperature　and　gas　pressure.The　characters　of　ion　nitriding　for　the　push　rod　and　the　way　to　solve　the　distortion　had　been　discussed.

关 键 词：铬钼钢 模具顶杆 离子渗氮 温度均匀性 

分 类 号：TG161.82[金属学及工艺—热处理] TG162.4[金属学及工艺—金属学]