Wetting Behavior and Interfacial Reactions in (Sn-9Zn)-2Cu/Ni Joints during Soldering and Isothermal Aging  

作　　者：Ning Zhao Haitao Ma Haiping Xie Lai Wang 

机构地区：[1]School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China

出　　处：《Journal of Materials Science & Technology》2009年第3期410-414,共5页材料科学技术（英文版）

基　　金：supported by the National Key Project of Scientific;Technical Supporting Programs during the 11th Five-year Plan (No. 2006BAE03B02-2);NSFC Key Program (No. U0734006)

摘　　要：The wetting property of （Sn-9Zn）-2Cu （wt pct） on Ni substrate and the evolution of interracial microstructure in （Sn-9Zn）-2Cu/Ni joints during soldering as well as isothermal aging were studied. The wetting ability of eutectic Sn-gZn solder on Ni substrate was markedly improved by adding 2 wt pct Cu into this solder alloy. Plate-like Cu5Zn8 intermetallic compounds （IMCs） were detected in （Sn-9Zn）-2Cu solder matrix. A continuous NisZn21 IMC layer was formed at （Sn-9Zn）-2Cu/Ni interface after soldering. This IMC layer kept its type and integrality even after aging at 170℃ for up to 1000 h. At the early aging stage （before 500 h）, the IMC layer grew fast and its thickness followed a linear relationship with the square root of aging time. Thereafter, however, the thickness increased very slowly with longer aging time. When the joints were aged for 1000 h, a new IMC phase, （Cu,Ni）5Zn8, was found in the matrix near the interface. The formation of （Cu,Ni）5Zns phase can be attributed to the diffusion of Ni atoms into the solder matrix from the substrate.The wetting property of （Sn-9Zn）-2Cu （wt pct） on Ni substrate and the evolution of interracial microstructure in （Sn-9Zn）-2Cu/Ni joints during soldering as well as isothermal aging were studied. The wetting ability of eutectic Sn-gZn solder on Ni substrate was markedly improved by adding 2 wt pct Cu into this solder alloy. Plate-like Cu5Zn8 intermetallic compounds （IMCs） were detected in （Sn-9Zn）-2Cu solder matrix. A continuous NisZn21 IMC layer was formed at （Sn-9Zn）-2Cu/Ni interface after soldering. This IMC layer kept its type and integrality even after aging at 170℃ for up to 1000 h. At the early aging stage （before 500 h）, the IMC layer grew fast and its thickness followed a linear relationship with the square root of aging time. Thereafter, however, the thickness increased very slowly with longer aging time. When the joints were aged for 1000 h, a new IMC phase, （Cu,Ni）5Zn8, was found in the matrix near the interface. The formation of （Cu,Ni）5Zns phase can be attributed to the diffusion of Ni atoms into the solder matrix from the substrate.

关 键 词：Lead-free solder Interfacial reaction Intermetallic compounds AGING 