Mssbauer study of the field induced uniaxial anisotropy in electro-deposited FeCo alloy films  

作　　者：李志伟 杨旭 王海波 刘忻 李发伸 

机构地区：[1]Institute of Applied Magnetics,Key Laboratory for Magnetism and Magnetic Materials of the Ministry of Education,Lanzhou University

出　　处：《Chinese Physics B》2009年第11期4829-4833,共5页中国物理B（英文版）

基　　金：Project supported by the National Natural Science Foundation of China (Grant No 10774061)

摘　　要：Thin ferromagnetic films with in-plane magnetic anisotropy are promising materials for obtaining high microwave permeability. The paper reports a MSssbauer study of the field induced in-plane uniaxial anisotropy in electro-deposited FeCo alloy films. The FeCo alloy films were prepared by the electro-deposition method with and without an external magnetic field applied parallel to the film plane during deposition. Vibrating sample magnetometry and MSssbauer spectroscopy measurements at room temperature indicate that the film deposited in external field shows an in-plane uniaxial anisotropy with an easy direction coinciding with the external field direction and a hard direction perpendicular to the field direction, whereas the film deposited without external field does not show any in-plane anisotropy. MSssbauer spectra taken in three geometric arrangements show that the magnetic moments are almost constrained in the film plane for the film deposited with applied magnetic field. Also, the magnetic moments tend to align in the direction of the applied external magnetic field during deposition, indicating that the observed anisotropy should be attributed to directional ordering of atomic pairs.Thin ferromagnetic films with in-plane magnetic anisotropy are promising materials for obtaining high microwave permeability. The paper reports a MSssbauer study of the field induced in-plane uniaxial anisotropy in electro-deposited FeCo alloy films. The FeCo alloy films were prepared by the electro-deposition method with and without an external magnetic field applied parallel to the film plane during deposition. Vibrating sample magnetometry and MSssbauer spectroscopy measurements at room temperature indicate that the film deposited in external field shows an in-plane uniaxial anisotropy with an easy direction coinciding with the external field direction and a hard direction perpendicular to the field direction, whereas the film deposited without external field does not show any in-plane anisotropy. MSssbauer spectra taken in three geometric arrangements show that the magnetic moments are almost constrained in the film plane for the film deposited with applied magnetic field. Also, the magnetic moments tend to align in the direction of the applied external magnetic field during deposition, indicating that the observed anisotropy should be attributed to directional ordering of atomic pairs.

关 键 词：ELECTRO-DEPOSITION FeCo film uniaxial anisotropy MSssbauer spectra 