低温区变形温度对含Nb钢奥氏体转变的影响  

Effect of Deformation Temperature on Austenite Transformation of Nb Microalloyed Steel

作　　者：董毅[1] 孙浩[2] 宋振官[2] 许云波[1] 吴迪[1] 

机构地区：[1]东北大学轧制技术及连轧自动化国家重点实验室,辽宁沈阳110004 [2]济南钢铁股份有限公司技术中心,山东济南250101

出　　处：《轧钢》2009年第6期1-4,共4页Steel Rolling

基　　金：国家自然科学基金资助项目(50504007);国家科技支撑计划项目(2007BAE51B07)

摘　　要：通过单道次压缩及冷却试验,研究了低温区变形温度对具有超细原始奥氏体晶粒的含Nb钢组织的影响。结果表明,在给定的试验条件下,试验钢的真应力-真应变曲线出现峰值,且峰值应力随温度的增加先增大再减小;随着变形温度的降低,组织中铁素体晶粒得到细化;在低于Ar_3温度下变形时,铁素体晶粒尺寸差异增大,铁素体硬度值分布较分散。Effect of deformation temperature on austenite transformation of Nb microalloyed steel with ultrafine initial austenite grain was studied by single hit compression and cooling tests. The results showed that the stress-strain curve present peaks, with the increasing of the deformation temperature, the peak stress increases first and then decreases; With the decreasing of the deformation temperature, the ferrite grain was refined; When the deformation temperature decreases to 750℃and 720℃ respectively, below Ar3, the difference of ferrite grain size was magnification, and the degree of the ferrite grain hardness dispersed distribute.

关 键 词：超细晶粒 含NB钢 变形温度 峰值应力 组织 

分 类 号：TG142.15[一般工业技术—材料科学与工程]