500℃下中国低活化马氏体钢电子辐照缺陷行为的研究  

Study on the defect evolution of China low martensitic steel during electron irradiation at 500 ℃

作　　者：乔建生[1,2] 刘永利[2] 万发荣[1,3] 

机构地区：[1]北京科技大学材料科学与工程学院材料物理与化学系,北京100083 [2]邢台学院初等教育学院,河北邢台054000 [3]北京新能源材料与技术重点实验室,北京100083

出　　处：《核科学与工程》2009年第4期341-348,354,共9页Nuclear Science and Engineering

基　　金：国家自然科学基金资助项目(50771017);国家重点基础研究发展计划基金资助项目(2007ID102)

摘　　要：利用超高压透射电子显微镜在500℃对两种不同成分的CLAM钢进行了小剂量的辐照实验,研究CLAM钢的辐照效应。发现在高能电子的辐照下,1号CLAM钢的微观结构发生了变化,产生了大量的位错环,研究了位错环形核和长大的规律;2号CLAM钢的微观结构也发生了变化,先产生位错环,而后形成了位错网络。A new version of reduced activation ferritic/martensitic steel, i.e. China low activation martensitic （CLAM） steel, was irradiated by high energy electron at 500℃. Irradiation effects were investigated with high voltage electron microscope. The results indicate that dislocation loops nucleate and grow up on the dislocations and other sites in 1 # CLAM steel during irradiation. In 2 # CLAM steel, dislocation loops were also induced and then evolved to dislocation net.

关 键 词：核聚变 辐照效应 位错环 

分 类 号：TG142.24[一般工业技术—材料科学与工程] TB383[金属学及工艺—金属材料]