纳米ATO粉体的制备及性能表征  

Preparation and characterization of nanometer ATO powder

作　　者：高桂兰[1] 段学成[2] 

机构地区：[1]上海第二工业大学城市建设与环境工程学院,上海201209 [2]中南大学材料科学与工程学院,长沙410083

出　　处：《化工新型材料》2010年第2期15-17,共3页New Chemical Materials

基　　金：国家863高技术科技研究发展计划项目(2002AA302606)

摘　　要：以SnCl4.5H2O和SbCl3为原料,采用化学共沉淀法制备了纳米级锑掺杂二氧化锡(ATO)粉体。研究了制备过程溶液pH值对ATO粉体粒径的影响。运用差热-热重(DTA-TG)、X射线衍射(XRD)、扫描电镜(SEM)等测试方法对粉体的热分解情况、晶型、粒径及形貌进行了表征。研究结果表明,ATO粉体为四方金红石型结构,平均粒径为60nm左右,团聚较少。Nanometer-sized ATO（antimony doped tin oxide） powder was prepared by a chemical coprecipitation method,using SnCl4·5H2O and SbCl3 as starting materials.The influence of terminal pH value on the particle size was discussed.The powder was examined by DTA-TG,XRD and SEM techniques to investigate its thermal decomposition,crystal phase composition,particle size and crystal appearance characteristics.The results showed that ATO powder prepared was tetrahedral rutile structure with low agglomeration.The average particle size was 60nm.

关 键 词：ATO 化学共沉淀法 纳米粉体 

分 类 号：TB383.1[一般工业技术—材料科学与工程]