Characteristic and Mitigation of Concrete Shrinkage Related to Moisture Migration

作　　者：乔墩[1] 钱觉时[1] 党玉栋[1] 贾兴文[1] 

机构地区：[1]重庆大学材料科学与工程学院,重庆400045

出　　处：《材料导报》2010年第17期79-83,95,共6页Materials Reports

基　　金：西部交通建设科技项目(2009318000033);重庆市科技项目(CSTC2009AC6204)

摘　　要：因水分迁移引起的收缩如果过大会引起混凝土开裂,从而影响混凝土的耐久性。通过分析混凝土中水分迁移可能引起的混凝土变形类型与内在影响因素以及引起开裂的条件,讨论了内养护和减缩剂用于混凝土成型后收缩控制的效果以及存在的问题,并提出了水分迁移引起的混凝土收缩、裂缝的研究及控制应注意的问题。Excessive shrinkage of concrete related to moisture migration will result in cracking, which affects markedly the durability of concrete. Through analyzing the essential types, influence factors and conditions leading to cracking of the volume change resulting from the moisture migration in concrete, the actions and shortcomings of the internal curing and a shrinkage reducing admixture used to reduce the shrinkage of concrete are discussed. Finally, the emphases on the mechanism and mitigation of the shrinkage and shrinkage cracking of concrete in the future are suggested.

关 键 词：混凝土 收缩裂缝 水分迁移 内养护 减缩剂(SRA) 

分 类 号：TU528[建筑科学—建筑技术科学]