LF6铝合金搅拌摩擦焊焊缝中S曲线对接头拉伸性能的影响  

Influence of S-type Curve in Friction Stir Welds on Tensile Properties of Welded Joint of Aluminum Alloy LF6

作　　者：刘耀[1] 邢丽[1] 杨成刚[1] 栾国红[2] 董春林[2] 

机构地区：[1]南昌航空大学航空制造工程学院,江西南昌330063 [2]北京航空制造工程研究所,北京100024

出　　处：《热加工工艺》2010年第17期139-141,共3页Hot Working Technology

基　　金：航空科学基金项目(20071156003)

摘　　要：在铝合金搅拌摩擦焊中,当焊接规范参数选取不当时,焊缝中会出现一种S形曲线。采用圆柱右螺纹搅拌头,对铣去对接面氧化膜和不铣去对接面氧化膜的试样分别进行搅拌摩擦焊试验,研究焊缝中S线对接头性能的影响。结果表明:焊缝中的S线对接头的拉伸性能有影响。含有S线的试样沿焊缝上的S线断裂,断面呈"S"状;焊缝中无S线的试样在焊核中断裂,断面呈45°。焊缝中的S线使接头的强度下降。The S-type curve appeared in the weld while welding parameters were not optimal in the aluminum fric-tion stir welding.The influence of S-type curve on the tensile properties of the joint was investigated by a pin with clockwise screw thread with and without oxide layer.The results show that S-type curve has an effect on the tensile properties of the joint.The tensile speciments with S-type curve all fracture along the zigzag-curve in the weld and the fracture shows in ＂S＂ shape.The S-type curve in the weld makes the tensile property of the joint decrease.

关 键 词：搅拌摩擦焊 S曲线 力学性能 LF6铝合金 

分 类 号：TG456[金属学及工艺—焊接]