铜单晶的定向方法研究  

Studies of Orientation on Copper Single Crystal

作　　者：唐世红[1] 赵北君[1] 朱世富[1] 肖怀安[1] 姚超[1] 何知宇[1] 陈宝军[1] 

机构地区：[1]四川大学材料科学与工程学院,成都610064

出　　处：《人工晶体学报》2011年第2期329-333,共5页Journal of Synthetic Crystals

摘　　要：采用改进的垂直布里奇曼法生长出外观完整、表面光滑、尺寸为15 mm×35 mm的Cu单晶体,报道了一种铜单晶定向的新方法。将生长出的铜晶锭在浓度为40%的硝酸溶液中浸蚀10 min左右,晶锭表面出现取向一致的反光面,用激光正反射法对其表面的反光面进行初步定向,再参照X射线衍射回摆谱对晶面进行修正,得到了铜晶体的(111)、(200)和(220)晶面,进而得到任意所需的晶面。该方法对于制作铜单晶器件具有重要参考价值。An integral copper single crystal with the diameter of 15 mm and length of 35 mm was grown by modified vertical Bridgman method.A new method for orientation of copper single crystal was presented.After being immersed and corroded for about 10 min with nitrate,the copper crystal ingot appeared reflective face with identical orientation on the surface.The（111）,（200） and（220） faces were obtained by the laser bidirectional reflection technique and X-ray diffraction（XRD） analysis,and then the other faces can be determined.The proposed procedure can provide basis for fabricating copper crystal devices.

关 键 词：铜单晶 定向 激光正反射法 X射线衍射 

分 类 号：O786[理学—晶体学]