多省并醌高介电聚合物的结构与特性的研究  

Study on structure and character of polyacene quinine radical polymer

作　　者：郑华靖[1] 唐先忠[1] 蒋亚东[1] 阮政[1] 

机构地区：[1]电子科技大学光电信息学院,四川成都610054

出　　处：《功能材料》2011年第10期1855-1860,共6页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(60372002)

摘　　要：采用未见文献报道的NaCl/AlCl3熔盐法合成多省并醌聚合物,并与常规硝基苯溶剂法进行对比,分析了聚合物的结构与热稳定性,测试了样品的介电常数与介电损耗。研究结果表明多省并醌聚合物热稳定性很好,5%质量损失温度>380℃。20Hz下熔盐法合成的聚合物介电常数达10471;在硝基苯中所得聚合物的介电常数为9.55。多省并醌聚合物的介电常数随外加电场频率升高而降低。A kind of molten salt NaCl/AlCl3,rarely reported in the synthesis of polymer was used to synthesize PAQR,which was compared with the one got in nitrobenzene.The structure and thermal stability of polymers have been studied as well as the dielectric constant.The results indicate that PAQR shows good thermal stability.The polymer synthesized in NaCl/AlCl3 exhibits huge dielectric constant which is over 10,000 when the frequency is 20Hz while the one of polymer synthesized in nitrobenzene is below 10.The dielectric constant of PAQR decreases rapidly as the frequency increases.Besides,two new monomers of anthraquinone 1,4-bis（octyloxy） anthracene-9,10-dione and 1,4-dibutoxyanthracene-9,10-dione are synthesized and characterized by FT-IR,1H NMR spectra and elemental analysis.Results of DSC and TG indicate melting points of two monomers are blow 130℃ and the 5% thermal decomposition temperatures are more than 200℃.

关 键 词：多省并醌聚合物 熔盐法 高介电常数 热稳定性 

分 类 号：O631[理学—高分子化学]