原位聚合法制备压敏型微胶囊及其应用研究  

Study on the Preparation Process of Pressure Sensitive Microcapsules by In-Situ Polymerization and Its Application

作　　者：司伟锋[1] 陈港[1] 

机构地区：[1]华南理工大学制浆造纸工程国家重点实验室,广东广州510640

出　　处：《造纸科学与技术》2011年第6期64-69,共6页Paper Science & Technology

基　　金：国家973项目(2010CB732206);教育部新世纪人才支持计划(D08001Ⅲ);粤港关键领域重点突破项目(200849834)

摘　　要：探讨了压敏型微胶囊制备工艺的优化,通过正交实验法确定了最优工艺条件为:乳化时间1为35min,乳化转速为3200rpm,乳化时间2为8min。通过粒径分布检测和扫描电镜观察发现,在最优条件下制得的微胶囊粒径均匀(3-10μm),表面光滑致密,无粘连现象。将微胶囊涂在CF纸上无显色现象,说明微胶囊密封性能良好。通过打印显色实验说明自制的微胶囊显色密度已达无碳复写纸一等品要求。The optimization of the preparation process of pressure sensitive microcapsules were discussed, and the optimum conditions were determined by orthogonal experiment, which were as follows： the emulsification time of the first stage was 35min, the emulsion speed was 3200r/min, and the emulsification time of the second stage was 8min. By detecting the particle size distribution and SEM observation, it was found that the microcapsules prepared under the optimal condition had a uniform particle size （3-10μm） , smooth and dense surface and no adhesion phenomenon. The prepared microcapsules were coated on the CF papers and there was no color phenomenon, indi- cating good sealing performance of the microcapsules. By color printing experiment, it showed that the self-made microcapsules had reached the first-class product requirements of carbonless copy paper.

关 键 词：原位聚合 正交实验 三聚氰胺甲醛树脂 微胶囊 

分 类 号：TS727.2[轻工技术与工程—制浆造纸工程]