高强度FeCo软磁合金高温性能研究  

Studies of Properties of High Strength FeCo Alloys at High Temprature

作　　者：韩劲[1] 倪志铭[1] 王二敏[1] 杨根林[1] 

机构地区：[1]北京航空材料研究院,北京100095

出　　处：《金属功能材料》2012年第4期1-3,共3页Metallic Functional Materials

摘　　要：高强度FeCo合金经研制后,在室温下获得了较高的力学性能和磁性能。本文介绍了高强度FeCo合金在200～500℃的力学性能和磁性能测试结果,并和1J21、1J22牌号的FeCo合金测试结果进行了比较。高强度FeCo合金在500℃时,其饱和磁感应强度Bs大于2.0T,矫顽力Hc在130A/m左右,同时抗拉强度σb达到850MPa,屈服强度σ0.2超过400MPa,而1J21、1J22在400℃时屈服强度σ0.2约为300MPa左右。结果表明,高强度FeCo合金是一种综合性能优良的高饱和磁通软磁合金,能够满足先进飞机的设计技术要求。The high strength FeCo alloys were prepared that showed high mechanical properties and magnetic proper- ties. This paper introduced the studies of the new material＇s properties at high tempratures from 200℃ to 500℃which compared with 1J21 and 1J22 alloys. The results of high strength FeCo alloys at 500℃ showed fine proper- ties also： the saturation magnetic induction Bs kept greater than 2.0 T,the coereivity Hc was about 130 A/re,the ul- timate tensile strength ab reached 850 MPa, the yield strength a0. z kept greater than 400 MPa, surpass the yield strengths a0. z of 1J21 and 1J22 alloys of about 300 MPa at 400℃. The results indicated that the high strength FeCo alloys with fine synthetical properties could meet the requirment of high saturation flux for soft magnetic alloys apl- lied in the advanced aircrafts in the future.

关 键 词：软磁合金 高强度FeCo合金 高温软磁合金 多电飞机 内置启动/发电机 

分 类 号：TG132.271[一般工业技术—材料科学与工程] TM271.2[金属学及工艺—合金]