硅灰石填充保鲜膜的性能研究  

Research on Properties of Wollastonite Filled Frech-keeping Film

作　　者：闫成云[1] 韩永生[1] 

机构地区：[1]天津科技大学,天津300222

出　　处：《包装工程》2013年第1期18-21,25,共5页Packaging Engineering

摘　　要：为增加保鲜膜透气和透湿性能,以LLDPE/LDPE(质量比75∶25)为基材,以硅灰石为填料,制备了不同处理方式和不同添加量的硅灰石保鲜膜。结果表明:随着硅灰石添加量的增加,薄膜的拉伸强度和断裂伸长率逐渐降低,未经处理的硅灰石填充膜的透气和透湿量明显提高,经偶联剂和酸处理的硅灰石能很好地提高与树脂的相容性,薄膜的拉伸强度和断裂伸长率都高于未处理填充膜,且透气系数和透湿系数与空白膜相比也有明显改善。LLDPE/LDPE（75∶25,W/W） and wollastonite were used as the substrate and inorganic stuffing respectively to prepare fresh-keeping film of different treatments and different additives.The results showed that with the increase of added wollastonite amount,the tensile strength and elongation at break of the film decreases gradually,but oxygen rate and moisture content of the untreated film is improved a lot;the coupling agent and acid treatment improves the compatibility between wollastonite and the resin;the tensile strength and elongation at break of the treated film were better than the untreated,and oxygen rate and moisture permeability quantity are also improved obviously compared with the blank film.

关 键 词：硅灰石 保鲜膜 酸处理 

分 类 号：TB484.3[一般工业技术—包装工程] TB487