PVAc乳液黏度的影响因素研究  

Study on influence factors of PVAc emulsion viscosity

作　　者：杨猛 李长多 高阳 周树柏 

机构地区：[1]抚顺哥俩好化学有限公司,辽宁抚顺113217

出　　处：《中国胶粘剂》2013年第3期22-25,共4页China Adhesives

摘　　要：以聚乙烯醇(PVA)为保护胶体、过硫酸铵(APS)为引发剂、醋酸乙烯酯(VAc)和丙烯酸(AA)为共聚单体,采用种子乳液聚合法制备聚醋酸乙烯酯(PVAc)乳液;然后以PVA的型号、AA和APS含量、反应温度、搅拌速率和种子单体含量等作为试验因素,以乳液黏度作为考核指标,采用单因素试验法优选制备PVAc乳液的最优方案。结果表明:当PVA型号为1788、w(AA)=1.2%、w(APS)=0.4%、w(种子单体)=6.5%、搅拌速率为120 r/min和反应温度为80℃时,PVAc乳液的综合性能优于市售同类产品。With polyvinyl alcohol （PVA） as protective colloid, ammonium persulfate （APS） as initiator, vinyl acetate（VAc） and acrylic acid （AA） as comonomers,a polyvinyl acetate （PVAc） emulsion was prepared by seed- emulsion polymerization. Then,with PVA＇s types,hA and APS contents,reaction temperatures,mix round speeds and seed-monomer contents as experiment factors,emulsion viscosity as evaluation index,the optimal project of preparing PVAc emulsion was preferred by single-factor experiment. The results showed that the combination property of PVAc emulsion was better than that of marketed similar product when PVA＇s type was 1788,mass fractions of AA,APS and seed-monomer were 1.2% ,0.4% and 6.5% respectively,mix round speed and reaction temperature were 120 r/min and 80 ℃ respectively.

关 键 词：聚醋酸乙烯酯 白乳胶 黏度 乳液聚合 

分 类 号：TQ433.433[化学工程]