大豆基胶粘剂生产环保竹地板的工艺研究  

Technology for Manufacture of Bamboo Flooring with Soybean Adhesives

作　　者：袁少飞[1,2] 李琴[1] 张建[1] 朱劲[3] 

机构地区：[1]浙江省林业科学研究院,浙江省竹类研究重点实验室,浙江杭州310023 [2]南京林业大学,江苏南京210037 [3]浙江农林大学,浙江临安311300

出　　处：《浙江林业科技》2013年第2期5-9,共5页Journal of Zhejiang Forestry Science and Technology

基　　金：农业科技成果转化项目(2012T201-06);浙江省林业厅省院合作项目(2010SY04);浙江省重大科技专项重点农业项目(2011C12050);竹类研究创新团队建设(2012F20024)

摘　　要：研究了大豆基胶粘剂的热学性能,以及陈化时间、施胶量和热压工艺对竹地板性能的影响,结果表明,以陈化时间1 h,施胶量200 g/m2为宜,较佳的热压工艺参数为热压温度145℃,热压时间2.5 min/mm,热压正压力4 MPa,产品性能达到竹地板的国家标准要求,且甲醛释放量为0.07 mg/L,达到日本F★★★★标准。Tests were implemented on thermal properties of soybean adhesives, as well as on effect of aging time, glue consumption and hot-pressing technology on bamboo floor performance. The results showed that bamboo floor performance could mcct state standard requirements with the aging time of one hour, glue consumption of 200 g/㎡, hot-pressing temperature of 145℃, hot-pressing time of 2.5 rain/ram, hot-pressing positive pressure of 4 MPa. Formaldehyde emission of manufactured bamboo floor could accord Japanese F★★★★ standard.

关 键 词：大豆基胶粘剂 环保竹地板 工艺研究 

分 类 号：S784[农业科学—林学]