纤维棒直径对轴编C/C复合材料拉伸强度的影响  

Effects of Fiber Rod Diameters on Tensile Strength of 4D In-Plane C/C Composites

作　　者：李书良[1,2] 侯晓[1,2] 史宏斌[2] 

机构地区：[1]西北工业大学航天学院,陕西西安710072 [2]中国航天科技集团公司第四研究院第四十一所固体火箭发动机燃烧/热结构与内流场国防科技重点实验室,陕西西安710025

出　　处：《推进技术》2013年第6期817-821,共5页Journal of Propulsion Technology

基　　金："九七三"项目(61391)

摘　　要：为了研究增强相尺度对轴编C/C复合材料拉伸性能的影响,通过对具有不同直径纤维棒的材料微结构的观测,结合材料的细观和宏观力学性能实验,研究了纤维棒直径引起的材料拉伸性能变化。结果表明:在编织参数不变的情况下,纤维棒直径增加,棒内大尺度裂纹增多,降低了材料的拉伸强度,但模量变化不明显。In order to study the effects of enforced phase size on the tensile properties of 4D in-plane C/ C composite, the change of tensile properties caused by the varied fiber rod diameters was investigated by microstructure observation, meso-mechanics and macro-mechanics experiment. Results show that in the case of keeping the braid parameters, the cracks are increased with the fiber bundles diameters, this results in the decrease of the tensile strength of material. However, the modulus does not have a significant change with the fiber rod diameter varied.

关 键 词：纤维棒 力学性能 轴编C C复合材料 微结构 

分 类 号：V258.3[一般工业技术—材料科学与工程]