CdSe与CdSe/ZnS量子点合成及稀土掺杂  

Synthesis and rare earth doped of CdSe and CdSe/ZnS QDs

作　　者：薛霏[1] 孟宪权[1] 刘义鹤[1] 

机构地区：[1]武汉大学物理学院,武汉430072

出　　处：《功能材料》2014年第1期55-58,共4页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(11275144;J1210061)

摘　　要：在LSS(liquid-solid-solution)多相体系中制得了CdSe、CdSe/ZnS量子点和Eu掺杂的量子点。利用TEM、XRD、PL、EDS对产物进行了表征。TEM结果显示所得的量子点形貌规则、尺寸均匀。XRD结果显示CdSe/ZnS量子点呈六方晶系。PL结果对比表明,合适厚度壳层ZnS包覆后的CdSe量子点发光效率明显提高,发光峰的半高宽有大幅度提高,并分析了所得的结果。掺杂稀土元素Eu后,CdSe(Eu)量子点在红光区域产生了新的发光峰;而CdSe(Eu)/ZnS量子点在红光区域内没有出现发光峰,并阐明了这种现象的原因。CdSe,CdSe/ZnS and Eu doped QDs were synthesized in LSS system.The QDs were characterized by TEM,XRD,PL and EDS.The TEM results showed that the QDs had uniform size and morphology.And the results of XRD showed CdSe/ZnS QDs belonged to hexagonal crystal system.The PL of the samples proved that the CdSe QDs coated with suitable thickness ZnS had a remarkable rise in luminous efficiency and the FWHM （the full width half maximum）.And we analyzed this results.The CdSe QDs doped with Eu had a new emission peak in red area,while the CdSe（Eu）/ZnS QDs did not.We also clarified the causes of this phenome-non .

关 键 词：量子点 稀土掺杂 

分 类 号：O472.3[理学—半导体物理]