GⅠ-Ⅱ型粉浆涂塑铝瓷底层冠专用代型材料对铝瓷底层冠适合性影响的初步研究  

A Study on the Influence of Adaptation of Die Material to GⅠ-Ⅱ Slip Casting Aluminous Ceramic Base Coping Material.

作　　者：孟辉[1] 万乾炳[2] 巢永烈[2] 

机构地区：[1]云南省第一人民医院,云南昆明650032 [2]华西医科大学口腔医学院

出　　处：《口腔医学纵横》2001年第1期48-49,共2页Journal of Comprehensive Stomatology

摘　　要：目的 :了解GⅠ Ⅱ型铝瓷专用代型材料对铝瓷底层冠适合性的影响。方法 :采用片切后SMI体式显微镜观察测量的方法测量在专用代型材料上制作的GⅠ Ⅱ型铝瓷底层冠粘固后的边缘浮出量及粘固剂厚度值。结果 :粘固后铝瓷底层冠边缘浮出量为 44 .2 1μm ,整体粘固剂厚度为 42 .2 5 μm。 结论 :GⅠ Ⅱ型专用代型材料的凝固膨胀较好地补偿了铝瓷的烧结收缩 ,制作的铝瓷底层冠具有良好的边缘适合性。Objective:To observe the influence of GⅠ Ⅱ die material to the adaptation of aluminous ceramic base coping.Methods:Evaluate the adaptation of GⅠ Ⅱ slip casting aluminous ceramic base coping made on GⅠ Ⅱ die material with SMI stereomicroscopic.Results:The marginal discrepancy after cementation was 44.21μm,the mean thickness of cement after cementation was 42.25μm.Conclusion:GⅠ Ⅱ slip casting aluminous ceramic base coping made on GⅠ Ⅱ die material could obtain a good adaptation. [

关 键 词：牙科材料 GⅠ-Ⅱ型粉浆 铝瓷底层冠 适合性 代型 

分 类 号：R783.1[医药卫生—口腔医学]