苯并噁嗪树脂烧蚀性能的初步研究  

Primary Investigation on Ablative Properties of Benzoxazine Resins

作　　者：纪凤龙[1] 顾宜[1] 谢美丽[1] 罗永康[2] 余春安[2] 蔡建强[2] 

机构地区：[1]四川大学高分子科学与工程学院高分子材料工程国家重点实验室,成都610065 [2]航天材料及工艺研究所,北京100076

出　　处：《宇航材料工艺》2002年第1期25-29,共5页Aerospace Materials & Technology

摘　　要：对苯并嗪树脂作为烧蚀树脂的应用进行了研究。采用TGA对四种中间体固化树脂的成碳率进行了测量 ,表明含有多个嗪环的PBOZ中间体和含有两嗪环的MDABOZ固化树脂和DRBOZ固化树脂成碳率较高 ,达到 60 %以上 ,而含有一个嗪环的SRBOZ固化树脂的成碳率相对较低。在以SRBOZ中间体为主体的树脂体系中引入MDABOZ中间体、DRBOZ中间体和APPFBOZ中间体后树脂体系的粘度较低而其固化产物的交联密度明显提高 ,成碳率达到 60 %以上。小发动机烧蚀试验表明PBOZ固化树脂的耐烧蚀性能较好 ,能够作为烧蚀树脂 ;Applications of benzoxazines as ablative resins were studied in this paper.Char yields of four kinds of cured benzoxazine precursors were measured by TGA and the data showed that the char yields of multi benzoxazine PBOZ precursors and di benzoxazine MDABOZ, DRBOZ precursors were higher than 60%, but that of mono benzoxazine SRBOZ precursors was relatively low. By introducing MDABOZ , DRBOZ and APPFBOZ precursors into SRBOZ resin system ,resultant char yield was remarkably raised over 60%,and viscosity of the resin systems was still low. Small generator ablation tests indicated that cured PBOZ precursors exhibited good ablation resistance and cured SRBOZ resin system modified by di benzoxazine MDABOZ precursors,with low viscosity,was upgraded substantially in its ablation resistance.

关 键 词：苯并恶嗪树脂 烧蚀材料 成碳率 航天器防热技术 

分 类 号：V255.03[一般工业技术—材料科学与工程]