新型锂二次电池阴极材料Li(Al_(0.3)Co_(0.7))O_2的充放电特性  

Charge-discharge Character of a New Cathode Material Li(Al_xCo_(1-x))O_2 of Rechargeable Lithium Battery

作　　者：郝万军[1,2] 李畅[1] 徐晓光[1] 陈岗[1] 许武[2] 

机构地区：[1]吉林大学材料科学与工程学院,汽车材料教育部重点实验室,长春130023 [2]中国科学院长春光学精密机械与物理研究所,长春130021

出　　处：《吉林大学学报（理学版）》2002年第2期179-182,共4页Journal of Jilin University:Science Edition

基　　金：国家自然科学基金 (批准号 :197740 2 8);吉林大学青年基金

摘　　要：研究应用于锂二次电池阴极的新型高能量密度存贮材料 L i( Alx Co1- x) O2 的充放电特性 ,并与相同条件下制备的传统材料 L i Co O2 进行对比 .结果表明 ,70 0℃烧结的Li( Al0 .3 Co0 .7) O2 有较好的充放电平台 ,电化学容量大于同样条件下制备的 Li Co O2 .The charge-discharge characters of a new cathode material with a high energy storage density, Li(Al xCo 1-x)O 2, were investigated and compared with those of the traditional cathode material, LiCoO 2, which was prepared under the same conditions. The results show that Li(Al xCo 1-x)O 2 sintered at 700 ℃ has a higher charge-discharge flat potential plateau, and a higher capacity than LiCoO 2 has under the same conditions.

关 键 词：锂二次电池 阴极材料 Li(Al0.3Co0.7)O2 充放电特性 电化学容量 能量密度 循环特性 

分 类 号：TM911.1[电气工程—电力电子与电力传动] TM201.4[一般工业技术—材料科学与工程]