CSP流程试制50W270高牌号无取向硅钢织构的演变  

Texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP route

作　　者：唐伟[1,2] 项利[2] 仇圣桃[2] 王建军[1] 

机构地区：[1]安徽工业大学冶金与资源学院,马鞍山243002 [2]中国钢研科技集团连铸技术国家工程研究中心,北京100081

出　　处：《北京科技大学学报》2014年第9期1189-1194,共6页Journal of University of Science and Technology Beijing

基　　金：国家自然科学基金;宝山钢铁股份有限公司联合资助项目(50934009)

摘　　要：研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构.This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling, normalizing, cold rolling, and annealing processes. The texture in the whole process was measured and analyzed by electron back-scatter diffraction. It is found that the texture along the thickness direction in hot-rolled strips changes obviously： there are mainly copper, brass, and Goss textures in the surface layer; the 1 / 4 layer has weak Goss texture and rotating cube texture; γ-fiber texture, rotating cube texture, and weak α-fiber texture appear in the center layer. Compared with hot rolled strips, the texture changes little for the normalized strip surface and 1 / 4 layer, but rotating cube texture and α-fiber texture are enhanced in the center layer. Quite strongα-fiber texture and γ texture appear in every layer for cold-rolled strips. Compared with cold-rolled strips, α-fiber texture almost disap-pears, but cube texture and Goss texture appear in annealed strips.

关 键 词：硅钢 CSP工艺 织构 

分 类 号：TG142.77[一般工业技术—材料科学与工程]