NaClO/IPA体系制备单晶硅太阳能电池绒面的研究  

The research of sodium hypochlorite/isopropyl alcohol in texturing single crystalline silicon for solar energy cells

作　　者：孙东亚[1] 何丽雯[2] 廉冀琼[1] 

机构地区：[1]厦门理工学院材料科学与工程学院,福建厦门361024 [2]华侨大学材料科学与工程学院,福建厦门361021

出　　处：《厦门理工学院学报》2014年第5期25-29,34,共6页Journal of Xiamen University of Technology

基　　金：福建省中青年教师教育科研项目(JB14077)

摘　　要：采用NaClO和IPA体系对单晶硅各向异性腐蚀制备绒面.通过紫外可见光光度计和扫描电镜对硅绒面的反射率、形貌进行了表征.结果表明,当NaClO为10%(质量分数,下同),IPA为5%,腐蚀温度为80℃,腐蚀时间为15 min时,能够得到均匀单晶硅绒面,硅片平均反射率达15%左右;与传统的Na OH/IPA腐蚀体系相比,该工艺制得的单晶硅绒面结构反射率低,有利于太阳能电池性能的提高.A novel anisotropic etching process based on a composition of sodium hypochlorite （ NaClO） /isopropyl alcohol （ IPA） was used to etch the surface of single crystal wafer silicon for solar cells. The surface structure and reflectance were characterized by UV-visible spectroscopy and. scanning electron microscope The results suggested that a uniform pyramid structure could be formed and the average reflection of surface was about 15% under 10% NaClO（ in mass, the same below） /3% IPA solution at 80 ℃ for 15 min. Compared with wafers fabricated with the traditional industrial process of NaOH/IPA, we obtained wafers with lower reflectance which can improve the performance of solar energy cells.

关 键 词：次氯酸钠 硅制绒 各向异性腐蚀 太阳能电池 

分 类 号：TM914.4[电气工程—电力电子与电力传动]