烟秆/聚乙烯复合材料的制备工艺及其性能研究  

Research on Preparation Process and Performance of Tobacco Stem/Polyethylene Composites

作　　者：刘旭东 姚建龙 蒋永涛 

机构地区：[1]常州产品质量监督检验所,江苏常州213000

出　　处：《林业机械与木工设备》2015年第5期25-27,共3页Forestry Machinery & Woodworking Equipment

摘　　要：研究了以烟秆碎料和聚乙烯(PE)为原料制造木塑复合材料的生产工艺,探讨了木塑配比、热压温度、热压时间及板材密度对复合材料性能的影响。结果表明:复合板材的最优工艺参数是烟秆碎料:聚乙烯为6:4、热压时间10 min、热压温度160℃、热压压力10 MPa、试验板密度0.8 g/cm3、酒精用量为聚乙烯用量的3%。The process for producing tobacco stem /polyethylene composite is studied and the effect of wood/plastic ratio,hot pressing time and density on the performance of composites is discussed,with the result showing the optimal process parame-ters of the composites： crushed tobacco stem /polyethylene ratio,6：4;hot pressing time,10min;hot-pressing temperature, 160 ℃;hot pressing pressure,10 MPa;experimental board density,0.8 g/cm3,alcohol consumption,3% of polyethylene.

关 键 词：烟秆碎料 聚乙烯 板材性能 工艺参数 

分 类 号：TS612[轻工技术与工程]