氧化锆陶瓷表面化学浴制备钙磷涂层的研究  

The deposition of calcium phosphate coating on the surface of zirconia by chemical bath method

作　　者：张玲玲[1] 张祖太[1] 丁宁[1] 刘艳[1] 

机构地区：[1]首都医科大学口腔医学院口腔医学研究所,北京100050

出　　处：《北京口腔医学》2015年第3期121-123,共3页Beijing Journal of Stomatology

基　　金：国家自然科学基金(81371175);北京市自然科学基金(7152065)

摘　　要：目的用化学浴方法在氧化锆陶瓷表面制备钙磷涂层。方法在Na OH、EDTA、Na H2PO4·2H2O、Ca Cl2混合溶液中垂直放入氧化锆陶瓷片,从室温加热到65℃。在65℃分别保持10min、15min和20min,扫描电镜和能谱分析观察、分析氧化锆陶瓷表面形态及成分。结果 15min氧化锆陶瓷表面形成一层薄钙磷涂层,随着化学浴时间的延长,涂层颗粒直径和涂层厚度增加。结论化学浴方法在氧化锆陶瓷表面制备出钙磷涂层可行。Objective To deposit calcium phosphate coating on the surface of zirconia.Methods Zirconia samples were vertically immersed in the solution of NaOH, EDTA, NaH2PO4·2H2O, CaCl2 which was heated from room temperature to 65℃, kept at 65℃ for 10 minutes, 15 minutes, 20 minutes, respectively. Scanning electron microscope （ SEM） and energy dispersive spectrometer （ EDS） were used to observe and analyze the zirconia surfaces. Results A thin calcium phosphate layer was formed on the surface of zirconia. The coating grain diameter and thickness increased as the chemical bath time extended.Conclusion Chemical bath method can be used to deposit calcium phosphate coating on the zirconia surface for improving its biocompatibility.

关 键 词：氧化锆 化学浴 钙磷涂层 

分 类 号：R783.1[医药卫生—口腔医学]